Effect of LaCl3 addition on the hydrogen storage properties of MgH2

Author

Listed:
  • Ismail, M.

Abstract

In this study, the effect of LaCl3 on the hydrogen storage properties of MgH2 prepared by ball milling was investigated for the first time. It was found that the MgH2 + 10 wt.% LaCl3 sample started to decompose at around 300 °C, which was 50 °C lower than in as-milled MgH2. For desorption kinetics, the LaCl3-doped MgH2 composite sample released about 4.2 wt.% hydrogen at 320 °C after 5 min dehydrogenation, while the as-milled MgH2 only released about 0.2 wt.% hydrogen for the same temperature and time. Meanwhile, a hydrogen absorption capacity of 5.1 wt.% was reached at 300 °C in 2 min for the LaCl3-doped MgH2 sample. In contrast, the ball-milled MgH2 only absorbed 3.8 wt.% hydrogen at 300 °C in 2 min. The activation energy of dehydrogenation was 166.0 kJ/mol for the as-milled MgH2 and 143.0 kJ/mol for the 10 wt.% LaCl3-added MgH2, indicating that the LaCl3 additive decreased the activation energy for the hydrogen desorption of the MgH2. The improved hydrogen storage properties of the MgH2 in the presence of LaCl3 is believed to be due to the catalytic effects of the La–Mg alloy and MgCl2 that were formed in situ during the heating process.

Suggested Citation

  • Ismail, M., 2015. "Effect of LaCl3 addition on the hydrogen storage properties of MgH2," Energy, Elsevier, vol. 79(C), pages 177-182.
  • Handle: RePEc:eee:energy:v:79:y:2015:i:c:p:177-182
    DOI: 10.1016/j.energy.2014.11.001
    as

    Download full text from publisher

    File URL: http://www.sciencedirect.com/science/article/pii/S0360544214012559
    Download Restriction: Full text for ScienceDirect subscribers only

    File URL: https://libkey.io/10.1016/j.energy.2014.11.001?utm_source=ideas
    LibKey link: if access is restricted and if your library uses this service, LibKey will redirect you to where you can use your library subscription to access this item
    ---><---

    As the access to this document is restricted, you may want to search for a different version of it.

    References listed on IDEAS

    as
    1. Ding, Xiangqian & Zhu, Yunfeng & Wei, Lingjun & Li, Ying & Li, Liquan, 2013. "Synergistic hydrogen desorption of HCS MgH2 + LiAlH4 composite," Energy, Elsevier, vol. 55(C), pages 933-938.
    2. Fan, Mei-Qiang & Liu, Shu-sheng & Zhang, Yao & Zhang, Jian & Sun, Li-Xian & Xu, Fen, 2010. "Superior hydrogen storage properties of MgH2–10 wt.% TiC composite," Energy, Elsevier, vol. 35(8), pages 3417-3421.
    3. Principi, G. & Agresti, F. & Maddalena, A. & Lo Russo, S., 2009. "The problem of solid state hydrogen storage," Energy, Elsevier, vol. 34(12), pages 2087-2091.
    Full references (including those not matched with items on IDEAS)

    Citations

    Citations are extracted by the CitEc Project, subscribe to its RSS feed for this item.
    as


    Cited by:

    1. Zhang, Wei & Cheng, Ying & Han, Da & Han, Shumin, 2015. "The hydrogen storage properties of MgH2–Fe3S4 composites," Energy, Elsevier, vol. 93(P1), pages 625-630.
    2. El-Eskandarany, M. Sherif & Shaban, Ehab & Alsairafi, Ammar A., 2016. "Synergistic dosing effect of TiC/FeCr nanocatalysts on the hydrogenation/dehydrogenation kinetics of nanocrystalline MgH2 powders," Energy, Elsevier, vol. 104(C), pages 158-170.
    3. Dou, Binlin & Zhang, Hua & Cui, Guomin & He, Mingxing & Ruan, Chenjie & Wang, Zilong & Chen, Haisheng & Xu, Yujie & Jiang, Bo & Wu, Chunfei, 2019. "Hydrogen sorption and desorption behaviors of Mg-Ni-Cu doped carbon nanotubes at high temperature," Energy, Elsevier, vol. 167(C), pages 1097-1106.
    4. Kou, Huaqin & Luo, Wenhua & Huang, Zhiyong & Sang, Ge & Meng, Daqiao & Zhang, Guanghui & Chen, Changan & Luo, Deli & Hu, Changwen, 2015. "Fabrication and experimental validation of a full-scale depleted uranium bed with thin double-layered annulus configuration for hydrogen isotopes recovery and delivery," Energy, Elsevier, vol. 90(P1), pages 588-594.
    5. Yang, Tai & Wang, Peng & Li, Qiang & Xia, Chaoqun & Yin, Fuxing & Liang, Chunyong & Zhang, Yanghuan, 2018. "Hydrogen absorption and desorption behavior of Ni catalyzed Mg–Y–C–Ni nanocomposites," Energy, Elsevier, vol. 165(PA), pages 709-719.
    6. Shen, Xiaochen & Wang, Qing & Wu, Qingquan & Guo, Siqi & Zhang, Zhengyan & Sun, Ziyang & Liu, Baishu & Wang, Zhibin & Zhao, Bin & Ding, Weiping, 2015. "CoB supported on Ag-activated TiO2 as a highly active catalyst for hydrolysis of alkaline NaBH4 solution," Energy, Elsevier, vol. 90(P1), pages 464-474.
    7. El-Eskandarany, M. Sherif & Al-Matrouk, H. & Shaban, Ehab & Al-Duweesh, Ahmed, 2015. "Superior catalytic effect of nanocrystalline big-cube Zr2Ni metastable phase for improving the hydrogen sorption/desorption kinetics and cyclability of MgH2 powders," Energy, Elsevier, vol. 91(C), pages 274-282.
    8. Zhang, J. & Yu, X.F. & Mao, C. & Long, C.G. & Chen, J. & Zhou, D.W., 2015. "Influences and mechanisms of graphene-doping on dehydrogenation properties of MgH2: Experimental and first-principles studies," Energy, Elsevier, vol. 89(C), pages 957-964.

    Most related items

    These are the items that most often cite the same works as this one and are cited by the same works as this one.
    1. Zhang, Wei & Cheng, Ying & Han, Da & Han, Shumin, 2015. "The hydrogen storage properties of MgH2–Fe3S4 composites," Energy, Elsevier, vol. 93(P1), pages 625-630.
    2. Kou, Huaqin & Luo, Wenhua & Huang, Zhiyong & Sang, Ge & Meng, Daqiao & Zhang, Guanghui & Chen, Changan & Luo, Deli & Hu, Changwen, 2015. "Fabrication and experimental validation of a full-scale depleted uranium bed with thin double-layered annulus configuration for hydrogen isotopes recovery and delivery," Energy, Elsevier, vol. 90(P1), pages 588-594.
    3. Öz, Çisem & Coşkuner Filiz, Bilge & Kantürk Figen, Aysel, 2017. "The effect of vinegar–acetic acid solution on the hydrogen generation performance of mechanochemically modified Magnesium (Mg) granules," Energy, Elsevier, vol. 127(C), pages 328-334.
    4. Ma, Li-Juan & Wang, Jianfeng & Han, Min & Jia, Jianfeng & Wu, Hai-Shun & Zhang, Xiang, 2019. "Adsorption of multiple H2 molecules on the complex TiC6H6: An unusual combination of chemisorption and physisorption," Energy, Elsevier, vol. 171(C), pages 315-325.
    5. Kalamse, Vijayanand & Wadnerkar, Nitin & Chaudhari, Ajay, 2013. "Multi-functionalized naphthalene complexes for hydrogen storage," Energy, Elsevier, vol. 49(C), pages 469-474.
    6. El-Eskandarany, M. Sherif & Al-Matrouk, H. & Shaban, Ehab & Al-Duweesh, Ahmed, 2015. "Superior catalytic effect of nanocrystalline big-cube Zr2Ni metastable phase for improving the hydrogen sorption/desorption kinetics and cyclability of MgH2 powders," Energy, Elsevier, vol. 91(C), pages 274-282.
    7. Ding, Xiangqian & Zhu, Yunfeng & Wei, Lingjun & Li, Ying & Li, Liquan, 2013. "Synergistic hydrogen desorption of HCS MgH2 + LiAlH4 composite," Energy, Elsevier, vol. 55(C), pages 933-938.
    8. El-Eskandarany, M. Sherif & Shaban, Ehab & Alsairafi, Ammar A., 2016. "Synergistic dosing effect of TiC/FeCr nanocatalysts on the hydrogenation/dehydrogenation kinetics of nanocrystalline MgH2 powders," Energy, Elsevier, vol. 104(C), pages 158-170.
    9. Pedicini, R. & Schiavo, B. & Rispoli, P. & Saccà, A. & Carbone, A. & Gatto, I. & Passalacqua, E., 2014. "Progress in polymeric material for hydrogen storage application in middle conditions," Energy, Elsevier, vol. 64(C), pages 607-614.
    10. Sun, Qian & Zou, Meishuai & Guo, Xiaoyan & Yang, Rongjie & Huang, Haitao & Huang, Peng & He, Xiangdong, 2015. "A study of hydrogen generation by reaction of an activated Mg–CoCl2 (magnesium–cobalt chloride) composite with pure water for portable applications," Energy, Elsevier, vol. 79(C), pages 310-314.
    11. Fan, Mei-Qiang & Liu, Shu-sheng & Zhang, Yao & Zhang, Jian & Sun, Li-Xian & Xu, Fen, 2010. "Superior hydrogen storage properties of MgH2–10 wt.% TiC composite," Energy, Elsevier, vol. 35(8), pages 3417-3421.
    12. Chung, Kyong-Hwan, 2010. "High-pressure hydrogen storage on microporous zeolites with varying pore properties," Energy, Elsevier, vol. 35(5), pages 2235-2241.
    13. Meryem Sena Akkus, 2022. "Investigation of Hydrogen Production Performance Using Nanoporous NiCr and NiV Alloys in KBH 4 Hydrolysis," Energies, MDPI, vol. 15(24), pages 1-15, December.
    14. Weng, Baicheng & Wu, Zhu & Li, Zhilin & Yang, Hui, 2012. "Hydrogen generation from hydrolysis of MNH2BH3 and NH3BH3/MH (M=Li, Na) for fuel cells based unmanned submarine vehicles application," Energy, Elsevier, vol. 38(1), pages 205-211.
    15. Valero-Pedraza, María José & Martín-Cortés, Alexandra & Navarrete, Alexander & Bermejo, María Dolores & Martín, Ángel, 2015. "Kinetics of hydrogen release from dissolutions of ammonia borane in different ionic liquids," Energy, Elsevier, vol. 91(C), pages 742-750.
    16. Jayalakshmi, S. & Vasantha, V.S. & Fleury, E. & Gupta, M., 2012. "Characteristics of Ni–Nb-based metallic amorphous alloys for hydrogen-related energy applications," Applied Energy, Elsevier, vol. 90(1), pages 94-99.
    17. Xiao, Jinsheng & Tong, Liang & Bénard, Pierre & Chahine, Richard, 2020. "Thermodynamic analysis for hydriding-dehydriding cycle of metal hydride system," Energy, Elsevier, vol. 191(C).
    18. Yang, Weijuan & Zhang, Tianyou & Liu, Jianzhong & Wang, Zhihua & Zhou, Junhu & Cen, Kefa, 2015. "Experimental researches on hydrogen generation by aluminum with adding lithium at high temperature," Energy, Elsevier, vol. 93(P1), pages 451-457.
    19. Pukazhselvan, D. & Hudson, M. Sterlin Leo & Sinha, A.S.K. & Srivastava, O.N., 2010. "Studies on metal oxide nanoparticles catalyzed sodium aluminum hydride," Energy, Elsevier, vol. 35(12), pages 5037-5042.
    20. Wang, Feng & Li, Rongfeng & Ding, Cuiping & Tang, Wukui & Wang, Yibo & Xu, Shimeng & Yu, Ronghai & Wang, Zhongmin, 2017. "Enhanced hydrogen storage properties of ZrCo alloy decorated with flower-like Pd particles," Energy, Elsevier, vol. 139(C), pages 8-17.

    Corrections

    All material on this site has been provided by the respective publishers and authors. You can help correct errors and omissions. When requesting a correction, please mention this item's handle: RePEc:eee:energy:v:79:y:2015:i:c:p:177-182. See general information about how to correct material in RePEc.

    If you have authored this item and are not yet registered with RePEc, we encourage you to do it here. This allows to link your profile to this item. It also allows you to accept potential citations to this item that we are uncertain about.

    If CitEc recognized a bibliographic reference but did not link an item in RePEc to it, you can help with this form .

    If you know of missing items citing this one, you can help us creating those links by adding the relevant references in the same way as above, for each refering item. If you are a registered author of this item, you may also want to check the "citations" tab in your RePEc Author Service profile, as there may be some citations waiting for confirmation.

    For technical questions regarding this item, or to correct its authors, title, abstract, bibliographic or download information, contact: Catherine Liu (email available below). General contact details of provider: http://www.journals.elsevier.com/energy .

    Please note that corrections may take a couple of weeks to filter through the various RePEc services.

    IDEAS is a RePEc service. RePEc uses bibliographic data supplied by the respective publishers.