Analysis of the Bowing Phenomenon for Thin c-Si Solar Cells using Partially Processed c-Si Solar Cells

Author

Listed:
  • Jong Rok Lim

    (Photovoltaics Laboratory, New and Renewable Energy Institute, Korea Institute of Energy Research, Daejeon 34129, Korea)

  • Sihan Kim

    (Department of Electrical and Electronics Engineering, Konkuk University, 120 Neungdong, Gwangjin, Seoul 05029, Korea)

  • Hyung-Keun Ahn

    (Department of Electrical and Electronics Engineering, Konkuk University, 120 Neungdong, Gwangjin, Seoul 05029, Korea)

  • Hee-Eun Song

    (Photovoltaics Laboratory, New and Renewable Energy Institute, Korea Institute of Energy Research, Daejeon 34129, Korea)

  • Gi Hwan Kang

    (Photovoltaics Laboratory, New and Renewable Energy Institute, Korea Institute of Energy Research, Daejeon 34129, Korea)

Abstract

The silicon wafers for solar cells on which the paste is deposited experience a bowing phenomenon. The thickness of commonly used c-Si wafers is 180 μm or more. When fabricating c-Si solar cells with this wafer thickness, the bowing value is 3 mm or less and the problem does not occur. However, for the thin c-Si solar cells which are being studied recently, the output reduction due to failure during manufacture and cracking are attributed to bowing. In generally, it is known that the bowing phenomenon arises mainly from the paste applied to the back side electrode of c-Si solar cells and the effects of SiNx (silicon nitride) and the paste on the front side are not considered significant. The bowing phenomenon is caused by a difference in the coefficient of expansion between heterogeneous materials, there is the effect of bowing on the front electrode and ARC. In this paper, a partially processed c-Si solar cell was fabricated and a bowing phenomenon variation according to the wafer thicknesses was confirmed. As a result of the experiment, the measured bow value after the firing process suggests that the paste on the front-side indicates a direction different from that of the back-side paste. The bow value increases when Al paste is deposited on SiNx. The fabricated c-Si solar cell was analyzed on basis of the correlation between the bowing phenomenon of the materials and the c-Si wafer using Stoney’s equation, which is capable of analyzing the relationship between bowing and stress. As a result, the bowing phenomenon of the c-Si solar cell estimated through the experiment that the back side electrode is the important element, but also the front electrode and ARC influence the bowing phenomenon when fabricating c-Si solar cells using thin c-Si wafers.

Suggested Citation

  • Jong Rok Lim & Sihan Kim & Hyung-Keun Ahn & Hee-Eun Song & Gi Hwan Kang, 2019. "Analysis of the Bowing Phenomenon for Thin c-Si Solar Cells using Partially Processed c-Si Solar Cells," Energies, MDPI, vol. 12(9), pages 1-12, April.
    • Handle: RePEc:gam:jeners:v:12:y:2019:i:9:p:1593-:d:226133
    as

    Download full text from publisher

    File URL: https://www.mdpi.com/1996-1073/12/9/1593/pdf
    Download Restriction: no
    File URL: https://www.mdpi.com/1996-1073/12/9/1593/
    Download Restriction: no
    ---><---

    References listed on IDEAS

    as
    1. Kaushika, N.D. & Rai, Anil K., 2007. "An investigation of mismatch losses in solar photovoltaic cell networks," Energy, Elsevier, vol. 32(5), pages 755-759.
    Full references (including those not matched with items on IDEAS)

    Most related items

    These are the items that most often cite the same works as this one and are cited by the same works as this one.
    1. Rehman, Shafiqur & El-Amin, Ibrahim, 2012. "Performance evaluation of an off-grid photovoltaic system in Saudi Arabia," Energy, Elsevier, vol. 46(1), pages 451-458.
    2. Siaw, Fei-Lu & Chong, Kok-Keong & Wong, Chee-Woon, 2014. "A comprehensive study of dense-array concentrator photovoltaic system using non-imaging planar concentrator," Renewable Energy, Elsevier, vol. 62(C), pages 542-555.
    3. Wang, Yaw-Juen & Hsu, Po-Chun, 2011. "An investigation on partial shading of PV modules with different connection configurations of PV cells," Energy, Elsevier, vol. 36(5), pages 3069-3078.
    4. Han, Changwoon & Lee, Hyeonseok, 2018. "Investigation and modeling of long-term mismatch loss of photovoltaic array," Renewable Energy, Elsevier, vol. 121(C), pages 521-527.
    5. Carrero, C. & Ramirez, D. & Rodríguez, J. & Castillo-Sierra, R., 2021. "Sensitivity analysis of loss resistances variations of PV generators applied to the assessment of maximum power point changes due to degradation," Renewable Energy, Elsevier, vol. 173(C), pages 351-361.
    6. Shen, Lu & Li, Zhenpeng & Ma, Tao, 2020. "Analysis of the power loss and quantification of the energy distribution in PV module," Applied Energy, Elsevier, vol. 260(C).
    7. Dobaria, Bhaveshkumar & Pandya, Mahesh & Aware, Mohan, 2016. "Analytical assessment of 5.05 kWp grid tied photovoltaic plant performance on the system level in a composite climate of western India," Energy, Elsevier, vol. 111(C), pages 47-51.
    8. Jiang, Joe-Air & Wang, Jen-Cheng & Kuo, Kun-Chang & Su, Yu-Li & Shieh, Jyh-Cherng & Chou, Jui-Jen, 2012. "Analysis of the junction temperature and thermal characteristics of photovoltaic modules under various operation conditions," Energy, Elsevier, vol. 44(1), pages 292-301.
    9. Ma, Tao & Guo, Zichang & Shen, Lu & Liu, Xing & Chen, Zhenwu & Zhou, Yong & Zhang, Xiaochun, 2021. "Performance modelling of photovoltaic modules under actual operating conditions considering loss mechanism and energy distribution," Applied Energy, Elsevier, vol. 298(C).
    10. Jeong Eun Park & Won Seok Choi & Dong Gun Lim, 2021. "Multi-Wire Interconnection of Busbarless Solar Cells with Embedded Electrode Sheet," Energies, MDPI, vol. 14(13), pages 1-19, July.
    11. Romênia G. Vieira & Fábio M. U. de Araújo & Mahmoud Dhimish & Maria I. S. Guerra, 2020. "A Comprehensive Review on Bypass Diode Application on Photovoltaic Modules," Energies, MDPI, vol. 13(10), pages 1-21, May.
    12. Yue, Gentian & Wu, Jihuai & Xiao, Yaoming & Lin, Jianming & Huang, Miaoliang & Lan, Zhang & Fan, Leqing, 2013. "Functionalized graphene/poly(3,4-ethylenedioxythiophene):polystyrenesulfonate as counter electrode catalyst for dye-sensitized solar cells," Energy, Elsevier, vol. 54(C), pages 315-321.
    13. Daraban, Stefan & Petreus, Dorin & Morel, Cristina, 2014. "A novel MPPT (maximum power point tracking) algorithm based on a modified genetic algorithm specialized on tracking the global maximum power point in photovoltaic systems affected by partial shading," Energy, Elsevier, vol. 74(C), pages 374-388.
    14. Wang, Ao & Xuan, Yimin, 2018. "A detailed study on loss processes in solar cells," Energy, Elsevier, vol. 144(C), pages 490-500.
    15. Ahmed Al Mansur & Md. Ruhul Amin & Kazi Khairul Islam, 2019. "Performance Comparison of Mismatch Power Loss Minimization Techniques in Series-Parallel PV Array Configurations," Energies, MDPI, vol. 12(5), pages 1-21, March.
    16. Kurt Michael Coetzer & Arnold Johan Rix & Pieter Gideon Wiid, 2022. "The Measurement and SPICE Modelling of Schottky Barrier Diodes Appropriate for Use as Bypass Diodes within Photovoltaic Modules," Energies, MDPI, vol. 15(13), pages 1-30, June.
    17. Claus, R. & López, M., 2022. "Key issues in the design of floating photovoltaic structures for the marine environment," Renewable and Sustainable Energy Reviews, Elsevier, vol. 164(C).
    18. Potnuru, Srinivasa Rao & Pattabiraman, Dinesh & Ganesan, Saravana Ilango & Chilakapati, Nagamani, 2015. "Positioning of PV panels for reduction in line losses and mismatch losses in PV array," Renewable Energy, Elsevier, vol. 78(C), pages 264-275.
    19. Zhang, Xiaoshun & Meng, Die & Cai, Jiahui & Zhang, Guiyuan & Yu, Tao & Pan, Feng & Yang, Yuyao, 2023. "A swarm based double Q-learning for optimal PV array reconfiguration with a coordinated control of hydrogen energy storage system," Energy, Elsevier, vol. 266(C).
    20. Zhenghai Liao & Dazheng Wang & Liangliang Tang & Jinli Ren & Zhuming Liu, 2017. "A Heuristic Diagnostic Method for a PV System: Triple-Layered Particle Swarm Optimization–Back-Propagation Neural Network," Energies, MDPI, vol. 10(2), pages 1-11, February.

    Corrections

    All material on this site has been provided by the respective publishers and authors. You can help correct errors and omissions. When requesting a correction, please mention this item's handle: RePEc:gam:jeners:v:12:y:2019:i:9:p:1593-:d:226133. See general information about how to correct material in RePEc.

    If you have authored this item and are not yet registered with RePEc, we encourage you to do it here. This allows to link your profile to this item. It also allows you to accept potential citations to this item that we are uncertain about.

    If CitEc recognized a bibliographic reference but did not link an item in RePEc to it, you can help with this form .

    If you know of missing items citing this one, you can help us creating those links by adding the relevant references in the same way as above, for each refering item. If you are a registered author of this item, you may also want to check the "citations" tab in your RePEc Author Service profile, as there may be some citations waiting for confirmation.

    For technical questions regarding this item, or to correct its authors, title, abstract, bibliographic or download information, contact: MDPI Indexing Manager (email available below). General contact details of provider: https://www.mdpi.com .

    Please note that corrections may take a couple of weeks to filter through the various RePEc services.

    IDEAS is a RePEc service. RePEc uses bibliographic data supplied by the respective publishers.