Mid-life degradation evaluation of polycrystalline Si solar photovoltaic modules in a 100 kWp grid-tied system in east-central India

Author

Listed:
  • Singh, Shravan Kumar
  • Chander, Nikhil

Abstract

This study presents the mid-life degradation evaluation of a 100 kWp grid-tied solar photovoltaic (PV) power plant which is in the eleventh year of its operation. The field evaluation includes the visual inspections to identify the extent of degradation present in the PV modules, and the measurement of field current-voltage (I–V) data for maximum power deviation of the operational PV modules. Significant visual degradations were observed in many PV modules like encapsulant discoloration, snail tracks and cell cracks, burn marks on the surface of the PV module, shattering of front PV glass due to lightning strike, discoloration on metallization, corroded metal frame and hot spots. The PV module having heavy snail tracks, visible cracks and burn marks on the surface showed the highest power reduction of 95.9 W with respect to the reference module. The power degradation rate of the reference PV modules, which had no apparent visible degradation, over a period of ten years, was found to be varying between 0.16%/year to 1.72%/year. This study would be helpful in better understanding of the various types of degradations affecting the PV modules operating in the composite climate regions of east-central India.

Suggested Citation

  • Singh, Shravan Kumar & Chander, Nikhil, 2022. "Mid-life degradation evaluation of polycrystalline Si solar photovoltaic modules in a 100 kWp grid-tied system in east-central India," Renewable Energy, Elsevier, vol. 199(C), pages 351-367.
    • Handle: RePEc:eee:renene:v:199:y:2022:i:c:p:351-367
    DOI: 10.1016/j.renene.2022.09.013
    as

    Download full text from publisher

    File URL: http://www.sciencedirect.com/science/article/pii/S0960148122013519
    Download Restriction: Full text for ScienceDirect subscribers only
    File URL: https://libkey.io/10.1016/j.renene.2022.09.013?utm_source=ideas
    LibKey link: if access is restricted and if your library uses this service, LibKey will redirect you to where you can use your library subscription to access this item
    ---><---

    As the access to this document is restricted, you may want to search for a different version of it.

    References listed on IDEAS

    as
    1. Bouaichi, Abdellatif & Alami Merrouni, Ahmed & Hajjaj, Charaf & Messaoudi, Choukri & Ghennioui, Abdellatif & Benlarabi, Ahmed & Ikken, Badr & El Amrani, Aumeur & Zitouni, Houssin, 2019. "In-situ evaluation of the early PV module degradation of various technologies under harsh climatic conditions: The case of Morocco," Renewable Energy, Elsevier, vol. 143(C), pages 1500-1518.
    2. Dag, H.I. & Buker, M.S., 2020. "Performance evaluation and degradation assessment of crystalline silicon based photovoltaic rooftop technologies under outdoor conditions," Renewable Energy, Elsevier, vol. 156(C), pages 1292-1300.
    Full references (including those not matched with items on IDEAS)

    Citations

    Citations are extracted by the CitEc Project, subscribe to its RSS feed for this item.
    as


    Cited by:

    1. Huang, Xin & Wang, He & Jiang, Xuefang & Yang, Hong, 2023. "Performance degradation and reliability evaluation of crystalline silicon photovoltaic modules without and with considering measurement reproducibility: A case study in desert area," Renewable Energy, Elsevier, vol. 219(P1).

    Most related items

    These are the items that most often cite the same works as this one and are cited by the same works as this one.
    1. Ameur, Arechkik & Berrada, Asmae & Bouaichi, Abdellatif & Loudiyi, Khalid, 2022. "Long-term performance and degradation analysis of different PV modules under temperate climate," Renewable Energy, Elsevier, vol. 188(C), pages 37-51.
    2. Alami Merrouni, Ahmed & Conceição, Ricardo & Mouaky, Ammar & Silva, Hugo Gonçalves & Ghennioui, Abdellatif, 2020. "CSP performance and yield analysis including soiling measurements for Morocco and Portugal," Renewable Energy, Elsevier, vol. 162(C), pages 1777-1792.
    3. Pramod Rajput & Maria Malvoni & Nallapaneni Manoj Kumar & O. S. Sastry & Arunkumar Jayakumar, 2020. "Operational Performance and Degradation Influenced Life Cycle Environmental–Economic Metrics of mc-Si, a-Si and HIT Photovoltaic Arrays in Hot Semi-arid Climates," Sustainability, MDPI, vol. 12(3), pages 1-20, February.
    4. Bouaichi, Abdellatif & El Amrani, Aumeur & Ouhadou, Malika & Lfakir, Aberrazak & Messaoudi, Choukri, 2020. "In-situ performance and degradation of three different photovoltaic module technologies installed in arid climate of Morocco," Energy, Elsevier, vol. 190(C).
    5. De Masi, Rosa Francesca & Gigante, Antonio & Ruggiero, Silvia & Vanoli, Giuseppe Peter, 2024. "Experimental and numerical approach for the evaluation of PV-system performance on energy and environmental behavior of nearly zero energy buildings: Case study in Mediterranean climate," Renewable Energy, Elsevier, vol. 227(C).
    6. Abdulwahab A. Q. Hasan & Ammar Ahmed Alkahtani & Seyed Ahmad Shahahmadi & Mohammad Nur E. Alam & Mohammad Aminul Islam & Nowshad Amin, 2021. "Delamination-and Electromigration-Related Failures in Solar Panels—A Review," Sustainability, MDPI, vol. 13(12), pages 1-23, June.
    7. Atsu, Divine & Seres, Istvan & Aghaei, Mohammadreza & Farkas, Istvan, 2020. "Analysis of long-term performance and reliability of PV modules under tropical climatic conditions in sub-Saharan," Renewable Energy, Elsevier, vol. 162(C), pages 285-295.
    8. Meena, Roopmati & Pareek, Arti & Gupta, Rajesh, 2024. "A comprehensive Review on interfacial delamination in photovoltaic modules," Renewable and Sustainable Energy Reviews, Elsevier, vol. 189(PA).
    9. Li, Baojie & Hansen, Clifford W. & Chen, Xin & Diallo, Demba & Migan-Dubois, Anne & Delpha, Claude & Jain, Anubhav, 2024. "A robust I–V curve correction procedure for degraded photovoltaic modules," Renewable Energy, Elsevier, vol. 224(C).
    10. Ben Seddik, Z. & Ben Taher, M.A. & Laknizi, A. & Ahachad, M. & Bahraoui, F. & Mahdaoui, M., 2022. "Hybridization of Taguchi method and genetic algorithm to optimize a PVT in different Moroccan climatic zones," Energy, Elsevier, vol. 250(C).
    11. Hassan Daher, Daha & Gaillard, Léon & Ménézo, Christophe, 2022. "Experimental assessment of long-term performance degradation for a PV power plant operating in a desert maritime climate," Renewable Energy, Elsevier, vol. 187(C), pages 44-55.
    12. Yazdani, Hamed & Yaghoubi, Mahmood, 2021. "Techno-economic study of photovoltaic systems performance in Shiraz, Iran," Renewable Energy, Elsevier, vol. 172(C), pages 251-262.
    13. Bouaichi, Abdellatif & Merrouni, Ahmed Alami & El Amrani, Aumeur & Jaeckel, Bengt & Hajjaj, Charaf & Naimi, Zakaria & Messaoudi, Choukri, 2022. "Long-term experiment on p-type crystalline PV module with potential induced degradation: Impact on power performance and evaluation of recovery mode," Renewable Energy, Elsevier, vol. 183(C), pages 472-479.
    14. Sina Herceg & Ismail Kaaya & Julián Ascencio-Vásquez & Marie Fischer & Karl-Anders Weiß & Liselotte Schebek, 2022. "The Influence of Different Degradation Characteristics on the Greenhouse Gas Emissions of Silicon Photovoltaics: A Threefold Analysis," Sustainability, MDPI, vol. 14(10), pages 1-15, May.
    15. Negri, Simone & Tironi, Enrico & Superti-Furga, Gabrio & Carminati, Marco, 2021. "VSC-based LVDC distribution network with DERs: Equivalent circuits for leakage and ground fault currents evaluation," Renewable Energy, Elsevier, vol. 177(C), pages 1133-1146.
    16. Piliougine, M. & Guejia-Burbano, R.A. & Petrone, G. & Sánchez-Pacheco, F.J. & Mora-López, L. & Sidrach-de-Cardona, M., 2021. "Parameters extraction of single diode model for degraded photovoltaic modules," Renewable Energy, Elsevier, vol. 164(C), pages 674-686.

    Corrections

    All material on this site has been provided by the respective publishers and authors. You can help correct errors and omissions. When requesting a correction, please mention this item's handle: RePEc:eee:renene:v:199:y:2022:i:c:p:351-367. See general information about how to correct material in RePEc.

    If you have authored this item and are not yet registered with RePEc, we encourage you to do it here. This allows to link your profile to this item. It also allows you to accept potential citations to this item that we are uncertain about.

    If CitEc recognized a bibliographic reference but did not link an item in RePEc to it, you can help with this form .

    If you know of missing items citing this one, you can help us creating those links by adding the relevant references in the same way as above, for each refering item. If you are a registered author of this item, you may also want to check the "citations" tab in your RePEc Author Service profile, as there may be some citations waiting for confirmation.

    For technical questions regarding this item, or to correct its authors, title, abstract, bibliographic or download information, contact: Catherine Liu (email available below). General contact details of provider: http://www.journals.elsevier.com/renewable-energy .

    Please note that corrections may take a couple of weeks to filter through the various RePEc services.

    IDEAS is a RePEc service. RePEc uses bibliographic data supplied by the respective publishers.