Abstract
This study investigates the effects of different pH environments on the durability of coir fiber-reinforced epoxy resin composites (CFRERCs). The CFRERCs were prepared by combining alkali-treated coir fibers with epoxy resin and exposing them to acidic, alkaline, pure water, and seawater environments for a 12-month corrosion test. The results show that an alkaline environment has the most significant impact on the tensile strength of CFRERCs, with a 55.06% reduction after 12 months. The acidic environment causes a 44.87% decrease in strength. In contrast, tensile strength decreases by 32.98% and 30.03% in pure water and seawater environments, respectively. The greatest reduction in tensile strain occurs in the alkaline environment, with a decrease of 36.45%. In the acidic environment, tensile strain decreases by about 25.56%, while in pure water and seawater, the reductions are 18.78% and 22.65%, respectively. In terms of stiffness, the alkaline environment results in a 49.51% reduction, while the acidic environment causes a 54.56% decrease. Stiffness decreases by 43.39% in pure water and 36.72% in seawater. Field emission scanning electron microscope (FE-SEM) analysis shows that corrosive agents in different pH environments cause varying degrees of damage to the microstructure of CFRERCs. In the acidic environment, corrosive agents erode the fiber–resin interface, leading to delamination and fiber breakage. In the alkaline environment, corrosive agents penetrate the fiber interior, increasing surface roughness and porosity. While pure water and seawater also cause some damage, their effects are relatively mild.
Suggested Citation
Liangyong Li & Juntong Wang & Tianxiang Peng, 2025.
"The Influence of pH Environments on the Long-Term Durability of Coir Fiber-Reinforced Epoxy Resin Composites,"
Sustainability, MDPI, vol. 17(1), pages 1-17, January.
Handle:
RePEc:gam:jsusta:v:17:y:2025:i:1:p:364-:d:1561042
Download full text from publisher
Corrections
All material on this site has been provided by the respective publishers and authors. You can help correct errors and omissions. When requesting a correction, please mention this item's handle: RePEc:gam:jsusta:v:17:y:2025:i:1:p:364-:d:1561042. See general information about how to correct material in RePEc.
If you have authored this item and are not yet registered with RePEc, we encourage you to do it here. This allows to link your profile to this item. It also allows you to accept potential citations to this item that we are uncertain about.
We have no bibliographic references for this item. You can help adding them by using this form .
If you know of missing items citing this one, you can help us creating those links by adding the relevant references in the same way as above, for each refering item. If you are a registered author of this item, you may also want to check the "citations" tab in your RePEc Author Service profile, as there may be some citations waiting for confirmation.
For technical questions regarding this item, or to correct its authors, title, abstract, bibliographic or download information, contact: MDPI Indexing Manager (email available below). General contact details of provider: https://www.mdpi.com .
Please note that corrections may take a couple of weeks to filter through
the various RePEc services.