Use of Tanδ and Partial Discharge for Evaluating the Cable Termination Assembly

Author

Listed:
  • Cihat Cagdas Uydur

    (Technical Sciences Vocational School, Trakya University, Edirne 22020, Turkey)

  • Oktay Arikan

    (Department of Electrical Engineering, Yildiz Technical University, Istanbul 34220, Turkey)

Abstract

It is known that the failure of cable terminations causes power outages and impairs system quality and continuity. Besides, serious economic losses on both the distribution and consumer sides occur. In this study, the dielectric behavior of the cable and the faults caused by the defects in the cable termination under overvoltage has been examined. As test samples, 12 kV XLPE insulated cable is used and they were aged at three (3*U 0 ) and five (5*U 0 ) times the rated voltage. After each aging cycle, dielectric parameters of the cable were measured by an OMIRCRON CPC100/CPTD1 device, and the partial discharge (PD) was measured by an OMICRON MPD600 device. In the measurements, it was observed that the cable was broken down at different aging cycle numbers as a result of defects in the cable termination due to weak workmanship. As a result of the measurements, it is concluded that defects in the cable termination give information about the increase in the probability of failure and the decrease of the cable lifetime. Consequently, it is concluded that fine workmanship and timely maintenance of cable terminations prevent the system from unwanted power outages and economic losses.

Suggested Citation

  • Cihat Cagdas Uydur & Oktay Arikan, 2020. "Use of Tanδ and Partial Discharge for Evaluating the Cable Termination Assembly," Energies, MDPI, vol. 13(20), pages 1-17, October.
  • Handle: RePEc:gam:jeners:v:13:y:2020:i:20:p:5299-:d:426632
    as

    Download full text from publisher

    File URL: https://www.mdpi.com/1996-1073/13/20/5299/pdf
    Download Restriction: no

    File URL: https://www.mdpi.com/1996-1073/13/20/5299/
    Download Restriction: no
    ---><---

    References listed on IDEAS

    as
    1. Krzysztof Lowczowski & Jozef Lorenc & Andrzej Tomczewski & Zbigniew Nadolny & Jozef Zawodniak, 2020. "Monitoring of MV Cable Screens, Cable Joints and Earthing Systems Using Cable Screen Current Measurements," Energies, MDPI, vol. 13(13), pages 1-28, July.
    2. Yunpeng Zhan & George Chen & Miao Hao & Lu Pu & Xuefeng Zhao & Sen Wang & Jian Liu, 2020. "Space Charge Measurement and Modelling in Cross-Linked Polyethylene," Energies, MDPI, vol. 13(8), pages 1-14, April.
    Full references (including those not matched with items on IDEAS)

    Most related items

    These are the items that most often cite the same works as this one and are cited by the same works as this one.
    1. Lixiao Mu & Xiaobing Xu & Zhanran Xia & Bin Yang & Haoran Guo & Wenjun Zhou & Chengke Zhou, 2021. "Autonomous Analysis of Infrared Images for Condition Diagnosis of HV Cable Accessories," Energies, MDPI, vol. 14(14), pages 1-15, July.
    2. Fuqiang Tian & Shuting Zhang & Chunyi Hou, 2021. "Effects of Trapping Characteristics on Space Charge and Electric Field Distributions in HVDC Cable under Electrothermal Stress," Energies, MDPI, vol. 14(5), pages 1-22, February.
    3. Luca Barbieri & Andrea Villa & Roberto Malgesini & Daniele Palladini & Christian Laurano, 2021. "An Innovative Sensor for Cable Joint Monitoring and Partial Discharge Localization," Energies, MDPI, vol. 14(14), pages 1-12, July.
    4. Aleksandra Schött-Szymczak & Krzysztof Walczak, 2021. "Impact of Cable Configuration on the Voltage Induced in Cable Screen during Work with One-Sidedly Ungrounded Cable Screen," Energies, MDPI, vol. 14(14), pages 1-14, July.

    Corrections

    All material on this site has been provided by the respective publishers and authors. You can help correct errors and omissions. When requesting a correction, please mention this item's handle: RePEc:gam:jeners:v:13:y:2020:i:20:p:5299-:d:426632. See general information about how to correct material in RePEc.

    If you have authored this item and are not yet registered with RePEc, we encourage you to do it here. This allows to link your profile to this item. It also allows you to accept potential citations to this item that we are uncertain about.

    If CitEc recognized a bibliographic reference but did not link an item in RePEc to it, you can help with this form .

    If you know of missing items citing this one, you can help us creating those links by adding the relevant references in the same way as above, for each refering item. If you are a registered author of this item, you may also want to check the "citations" tab in your RePEc Author Service profile, as there may be some citations waiting for confirmation.

    For technical questions regarding this item, or to correct its authors, title, abstract, bibliographic or download information, contact: MDPI Indexing Manager (email available below). General contact details of provider: https://www.mdpi.com .

    Please note that corrections may take a couple of weeks to filter through the various RePEc services.

    IDEAS is a RePEc service. RePEc uses bibliographic data supplied by the respective publishers.